New test is carried out in Lantec to consolidate process of laser welding.
In this case we are laser welding 0.3 thick Alu plates together.
First tries are done preparing butt welding tool with good results at 1.2 m/min. However tensile test results are giving low values for the expected target.
Secondly, overlap (0.3 + 0.3) welding shots are produce, lowering power and using 600 w pulsed power laser. Results as shown in the picture are more likely to be accepted by the customer. Additional challenge is to avoid heat damage on the outer side of the plate. By producing 0.4 mm welds (106 microns spot) and 0.5 mm penetration we see there is a steady process and good tensile resistance goal is achieve.
mercredi 25 octobre 2017 | Published in Blog First tries are done preparing butt welding tool with good results at 1.2 m/min. However tensile test results are giving low values for the expected target.
Secondly, overlap (0.3 + 0.3) welding shots are produce, lowering power and using 600 w pulsed power laser. Results as shown in the picture are more likely to be accepted by the customer. Additional challenge is to avoid heat damage on the outer side of the plate. By producing 0.4 mm welds (106 microns spot) and 0.5 mm penetration we see there is a steady process and good tensile resistance goal is achieve.
Last news
-
Nuevo cabezal de corte láser.
mercredi 14 août 2019 -
Soldadura láser de extintores
mercredi 22 mai 2019 -
Automation process for laser marking of components for the hardware industry
mardi 18 septembre 2018 -
Laser marking over covered cast steel
lundi 30 juillet 2018 -
Tests of laser welding on bronze and stainless steel
lundi 14 mai 2018